| Customization: | Available |
|---|---|
| Material: | Carbon Steel |
| Type: | Hexagon Head |
|
Still deciding? Get samples of $ !
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
The A193 B7 stud bolt is a fastener with threads on both ends. It is designed to be screwed into a fixed part at one end and to receive a nut on the other. In the petroleum and chemical industries, these products are used extensively for flange connections. The most common configuration involves a stud bolt with two nuts on either side, which serves as a replacement for the traditional bolt and nut assembly.
As you are no doubt aware, stud bolts are available in a variety of categories. The type used for flange connection is known as a flange stud bolt, and it has fully threaded, chambered ends. The theoretical length is measured from the thread. The continuous threaded stud bolt is very similar, except that it does not have chambered ends.
Stud Bolt Materials
The most common materials for stud bolts (for flanges) are ASTM A193 (grade B7, B8, B8M, B8T), ASTM A453 (grade 660), ASTM A320 (grade L7, L7M), and ASTM A182 (duplex and super duplex bolting). For aggressive fluids and environments, stud bolts can be coated with Xylan/PTFE, Zinc and other materials.
| Physical Element | ASTM A193 grade B7 (AISI 4140) | ASTM A193 grade B8 (AISI 304) | ASTM A193 grade B8M (AISI 316) |
|---|---|---|---|
| Carbon | 0.38 - 0.48% | 0.08% max | 0.08% max |
| Manganese | 0.75 - 1.00% | 2.00% max | 2.00% max |
| Phosphorus, max | 0.035% | 0.045% | 0.045% |
| Sulfur, max | 0.040% | 0.030% | 0.030% |
| Silicon | 0.15 - 0.35% | 1.00% max | 1.00% max |
| Chromium | 0.80 - 1.10% | 18.0 - 20.0% | 16.0 - 18.0% |
| Nickel | absent | 8.0 - 11.0% | 10.0 - 14.0% |
| Molybdenum | 0.15 - 0.25% | absent | 2.00 - 3.00% |
| ASTM A193 | Size | Min Tensile Strength (KSI) | Min Yield Strength (KSI) | Min Elongation (%) | RA % min | Max HBW | Max HRC |
|---|---|---|---|---|---|---|---|
| ASTM A193 grade B7 | Up to 2-1/2 | 125 | 105 | 16 | 50 | 321 | 35 |
| 2-5/8 - 4 | 115 | 95 | 16 | 50 | |||
| 4-1/8 - 7 | 100 | 75 | 18 | 50 | |||
| ASTM A193 grade B8 Class 1 | All | 75 | 30 | 30 | 50 | 223 | 35 |
| ASTM A193 grade B8M Class 1 | All | 75 | 30 | 30 | 50 | 223 | 96 |
| ASTM A193 grade B8 Class 2 | Up to 3/4 | 125 | 100 | 12 | 35 | 321 | 35 |
| 7/8 - 1 | 115 | 80 | 15 | 35 | |||
| 1-1/8 - 1-1/4 | 105 | 65 | 20 | 35 | |||
| 1-3/8 - 1-1/2 | 100 | 50 | 28 | 45 | |||
| ASTM A193 grade B8M Class 2 | Up to 3/4 | 110 | 95 | 15 | 45 | 321 | 35 |
| 7/8 - 1 | 100 | 80 | 20 | 45 | |||
| 1-1/8 - 1-1/4 | 95 | 65 | 25 | 45 | |||
| 1-3/8 - 1-1/2 | 90 | 50 | 30 | 45 |
The material chosen for the threaded stud and the hex nuts should be compatible. Materials for bolting sets shall be selected based on the process's working temperatures, as shown in the table below:
| TEMPERATURE °C ( °F ) | ||
| STUD BOLTS MATERIALS | MIN. | MAX. |
| CARBON STEEL | -29 (-20) | 300 (572) |
| A193 B7, L7 | -73 (-100) | 400 (752) |
| A193 B6 | 0 (32) | 500 (932) |
| A193 B8 | -200 (-325) | 575 (1067) |
| A193 B16 | 0 (32) | 520 (968) |
| A193 B17B | -29 (-20) | 650 (1202) |
| A913 Inconel 718 | 0 (32) | 750 (1382) |
| A453 Gr. 660 | -29 (20) | 538 (1000) |
Stud bolts can be coated to increase the resistance to corrosion. The most common types of coatings for stud bolts are listed below:
){kind=link}